Abstract
ISO 23146:2012 specifies a method for the determination of the fracture toughness of advanced technical ceramics. The procedure makes use of single-edge V-notched bars, which are loaded in four-point bending until failure. It is applicable to monolithic ceramics with a grain size or major microstructural feature size larger than about 1 µm.
The use of ISO 23146:2012 for yttria tetragonal zirconia polycrystal material (Y-TZP) is not recommended. The method might also be unsuitable for some other very tough or soft ceramics in which a sharp crack does not form at the root of the V-notch.
General information
-
Status: Under developmentStage: New project approved [10.99]
-
Edition: 3
-
Technical Committee :ISO/TC 206
- RSS updates
Life cycle
-
Previously
PublishedISO 23146:2012
-