Gears — Surface temper etch inspection after grinding, chemical method
Edition 3
2017-04
Preview
ISO 14104:2017
70396
недоступно на русском языке
Опубликовано (Версия 3, 2017)
Последний раз этот публикация был пересмотрен в  2022. Поэтому данная версия остается актуальной.

ISO 14104:2017

ISO 14104:2017
70396
Язык
Формат
CHF 96
Пересчитать швейцарские франки (CHF) в ваша валюта

Тезис

ISO 14104:2017 specifies procedures and requirements for the detection and classification of localized overheating on ground surfaces by chemical etch methods.

The process described in this document is typically used on ground surfaces; however, it is also useful for the detection of surface anomalies that result from post-heat treatment machining such as hard turning, milling and edge breaking (deburring) processes. Surface metallurgical anomalies caused by carburization or decarburization are also readily detectable with this process.

Some methods which have been used in the past are no longer recommended. Specifications are intended to be changed to use the methods in this document. These etching methods are more sensitive to changes in surface hardness than most hardness testing methods.

ISO 14104:2017 applies to steel parts such as gears, shafts, splines and bearings. It is not applicable to nitrided parts and stainless steels.

NOTE This process, although at times called "nital etch", is not intended to be confused with other processes also known as "nital etch".

The surface temper etch procedure is performed after grinding and before additional finishing operations such as superfinishing, shot peening and honing.

Общая информация

  •  : Опубликовано
     : 2017-04
    : Подтверждение действия международного стандарта [90.93]
  •  : 3
  • ISO/TC 60/SC 2
    21.200 
  • RSS обновления

Жизненный цикл

Появились вопросы?

Ознакомьтесь с FAQ